Payment & Shipping Terms:
|Vacuum Reaching Pressure:||10-3 Pa||Leakage Volume:||Less Than 10-9Pam3/sec|
|Injection Pressure:||Max. 0.1MPa||Highest Heating Temperature:||1500°C|
powder metallurgy manufacturing process,
powder metallurgy equipment
Amorphous Alloy Powder Production Equipment
Amorphous Alloy Powder Production Equipment is the magnetic material handling equipment that continuously produces amorphous alloy powder by using high-speed cooling method. The large-scale production is conducted under protective gas or vacuum condition. The produced powders mainly are used for electrics, electronic components, military industry etc..
Its working principle refers to that smelted metal is jetted onto quench cooling roller in high-speed rotation under given conditions in Ar gas environment, after vacuum exhausting, and then the amorphous thin band though quench cooling process.
Vacuum reaching pressure: 10-3 Pa (when filling with specimen and nozzle);
Leakage volume: less than 10-9Pam3/sec;
Injection pressure: Max. 0.1MPa;
Smelting capacity: 5~50g/based on iron;
Highest heating temperature: 1500°C;
Common heating temperature: 1200°C;
Cooling roller rotating speed: 100-500rpm;
High-frequency output: 5kW;
Output frequency: 100KHz.
Power supply: 3 phases, 220V, 13KVA (clients need to prepare voltage transformer for their own)
Cooling water: 25L/min, water pressure: 0.35MPa (backpressure: less than 0.1MPa)
Inert gas (Ar): displaced capacity 100L/per time, pressure 0.5MPa.
Contact Person: Easy