|Injection Pressure:||Max. 0.1MPa||Feeding Material:||10-3 Pa|
|Leakage Volume:||Less Than 10-9Pam3/sec||Smelting Capacity:||5~50g/based On Iron;|
|Common Heating Temperature:||1200°C||Highest Heating Temperature:||1500°C|
powder metallurgy equipment,
powder manufacturing process
Amorphous Alloy Powder Production Equipment 300 KG For Ti Base In Flame Plating
1. Amorphous Alloy Powder Production Equipment is the magnetic material processing equipment that continuously produces amorphous alloy powders by using high-speed cooling method.
2. The large-scale production is conducted under protective gas or vacuum condition. The produced powders are mainly used for electrics, electronic components, military industry etc..
Vacuum reaching pressure: 10-3 Pa (when filling with specimen and nozzle);
Leakage volume: less than 10-9Pam3/sec;
Injection pressure: max. 0.1MPa;
Smelting capacity: 5~50g/based on iron;
Highest heating temperature: 1500°C;
Common heating temperature: 1200°C;
Cooling roller rotating speed: 100-500rpm (single roller size: Φ200*20mm);
High-frequency output: 5kW;
Output frequency: 100KHz.
Power supply: 3 phases, 220V, 13KVA (clients need to prepare voltage transformer for their own)
Cooling water: 25L/min, water pressure: 0.35MPa (backpressure: less than 0.1MPa)
Inert gas (Ar): displaced capacity 100L/per time, pressure 0.5MPa.
Its working principle refers to that smelted metal is jetted onto quench cooling roller in high-speed rotation under given conditions in Ar gas environment after vacuum exhausting, and then the amorphous thin band is formed though quench cooling process.